- Conspectus
- Producta Commendata
- Ratio contractionis: 1,7:1 et 3,2:1
- Iners chemicus
- Resistentia ad frictionem et immersionem in oleo
- Summe igni-retardans
- Optiones parietis tenuis et extra tenuis adstant
- Continuum temperaturarum operativarum intervallum: −65 °C usque ad 260 °C
- Temperatura plenae recuperationis: 350 °C
- SAE-AMS-DTL-23053/13
- Color normalis: Translucidus (-X).
- Magnitudines speciales pro petitione habentur.
- Emballagium normale: In longitudinibus unius metri et viginti centimetrorum.
Eigenschaften
Operatio et installatio
Referentia Communis
Proprietates Producti
| Property | Postulationem | Test Methodi |
| Robur Tensile | 17,3 MPa min. | ASTM D2671 |
| Elongatio Ultima | 200 % min. | ASTM D2671 |
| Flexibilitas ad Temperaturam Infimam (4 h ad −65 °C) | Nullum fissuram. | ASTM D2671 |
| Shock Caloris (4 h ad 400 °C) | Nullum guttare, colare aut rimari. | ASTM D2671 |
|
Aetates Caloris (96 h ad 350 °C) Sequitur: Resistentia ad Tractionem Elongatio Ultima |
17,3 MPa min. 200 % min. |
ISO 188 ASTM D2671 ASTM D2671 |
| Fortitudo Dielectrica | 31,5 kV/mm min. | ASTM D2671 |
| Volumen resistivity | 10¹⁵ Ω·cm min. | ASTM D2671 |
Descriptio
Designatus est ad praebendam protectionem mechanicam componentium adversus altas temperaturas et fluida agressiva. Vulgo utitur ad protectionem catarum, ad alleviandam tensionem in terminis et connexionibus filorum, ad insulationem vel vestimentum fasciculorum filorum, ad protectionem punctorum soldatorum, ad involvendum componentia electronica, ad insulationem vel protectionem resistorum et capacitorum, ad protectionem anticorrosivam productorum metallicorum, etc.
Product Dimensiones
| Magnitudo | UT SUPPEDITATUR | Post Recuperationem | |
| D.I. (min.) | D.I. (max.) | Crassitudo parietis | |
| Ratio contrahendi 1,7:1 | |||
| 0.8 | 0.8 | 0.4 | 0.23±0.07 |
| 1 | 1 | 0.5 | 0.23±0.07 |
| 1.2 | 1.2 | 0.7 | 0.25±0.08 |
| 1.5 | 1.5 | 0.8 | 0.30±0.08 |
| 2 | 2 | 1.1 | 0.30±0.08 |
| 2.5 | 2.5 | 1.4 | 0.30±0.08 |
| 3 | 3 | 1.7 | 0.30±0.08 |
| 3.5 | 3.5 | 2 | 0.30±0.08 |
| 4 | 4 | 2.3 | 0.30±0.08 |
| 4.5 | 4.5 | 2.6 | 0.30±0.08 |
| 5 | 5 | 2.9 | 0.30±0.08 |
| 6 | 6 | 3.5 | 0.38±0.10 |
| 7 | 7 | 4.1 | 0.38±0.10 |
| 8 | 8 | 4.7 | 0.38±0.10 |
| 9 | 9 | 5.2 | 0.38±0.10 |
| 10 | 10 | 5.8 | 0.38±0.10 |
| 11 | 11 | 6.4 | 0.38±0.10 |
| 12 | 12 | 7 | 0.38±0.10 |
| 13 | 13 | 7.6 | 0.38±0.10 |
| 15 | 15 | 8.8 | 0.38±0.10 |
| Ratio contrahendi 3,2:1 | |||
| 5/64 | 2 | 0.6 | 0.23±0.07 |
| 1/8 | 3.2 | 1 | 0.30±0.08 |
| 3/16 | 4.8 | 1.2 | 0.30±0.08 |
| 1/4 | 6.4 | 1.6 | 0.30±0.08 |
| 3/8 | 9.5 | 2.4 | 0.30±0.08 |
| 1/2 | 12.7 | 3.7 | 0.38±0.10 |
| 5/8 | 15.9 | 4.5 | 0.38±0.10 |
| 3/4 | 19 | 5.7 | 0.38±0.10 |
| 1 | 25.4 | 7.1 | 0.38±0.10 |
| 1 1\/4 | 32 | 8.8 | 0.38±0.10 |
Dimensiones in mm. D.I. = Diameter Interior